Initial complex

°
T, C

CompositionMe/C

Ratio Me1:Me2:C

Ssp, m2/g

Morphology

[Co(en)3][Fe(ox)3]

550

60,7/23,6

1:0,9:3,6

93

hollow prisms

600

63,7/21,2

1:1:3

154

700

71,2/23

1:0,9:2,9

128

[Ni(NH3)6]3[Fe(CN)6]2

600

77/23

3:2:7,3

27,7

fine tangled filaments + spongy
aggregates

650

78/22

3:2:7

43,8

700

80/19

3:2:5,5

72,7

800

72,9/21,6

3:2:7

78,5

[Co(NH3)6][Fe(CN)6]

630

71/29

1:1:3,9

36,5

rod-like particles

800

70,8/27,5

1:1:3,7

35,7

[Co(NH3)6]4[Fe(CN)6]3

675

75,3/22,1

4:3:9,7

48

spongy masses

950

76/23

4:3:10,1

49,3

[Co(en)3][Fe(CN)6]

450

39/30

1:1:7,4

22

elongated nodules

700

60/40

1:1:6,5

–

[Co(en)3]4[Fe(CN)6]3

560

55/30

4:3:18,4

33

irregularly shaped debris

650

64,5/35

4:3:17,9

102

[Co(NH3)6]Cl[Cu (C7H4O3)2]

650

57,6/29

1:1:5,2

38.6

porous cellular formations

900

67,7/33

1:1:5

186

Initialcomplex

°
T, C

Yield, g C/g complex

ContentMe1+Me2,
%

Ssp, m2/g

d (Ssp), nm

d (Scherrer formula), nm

Morphology

[Co(en)3][Fe(ox)3]

550

0,37

255

15

Hollow prisms

600

0,36

263

15

700

0,45

328

12

[Ni(NH3)6]3[Fe(CN)6]2

600

0,30

224

14

Filamentous crystals

650

0,24

4,2 + 3,4

226

17

36

700

0,28

8,0 + 6,8

276

14

14

800

0,33

8,4 + 6,1

230

17

40

[Co(NH3)6][Fe(CN)6]

630

0,32

3,8 + 4,8

109

29

31

Tubular particles

800

0,31

2,3 + 3,0

109

31

31

[Co(NH3)6]4[Fe(CN)6]3

675

0,31

13,0 + 11,0

176

22

22

fine filament
conglomerate

950

0,31

11,6 + 9,4

150

26

26

[Co(en)3][Fe(CN)6]

450

0,31

13,3 +14,6

380

–

–

Sponge plates

700

0,61

13,0 +10,4

230

11

9

[Co(en)3]4[Fe(CN)6]3

560

0,46

25,4 +9,5

40

–

–

Irregularly shaped debris

650

0,52

16,4 +10,7

206

11

13

[Co(NH3)6]Cl[Cu(C7H4O3)2]

650

0,46

17

48

53

–

Large porous particles

900

0,33

undetected

466

8

–